Evaluation of local stress state due to grain-boundary sliding during creep within a crystal plasticity finite element multi-scale framework

内容摘要

Previous studies demonstrate that grain-boundary sliding could accelerate creep rate and give rise to large internal stresses that can lead to damage development, e.g. formation of wedge cracks. The present study provides more insight into the effects of grain-boundary sliding (GBS) on the deformation behaviour of realistic polycrystalline aggregates during creep, through the development of a computational framework which combines: i) the use of interface elements for sliding at grain boundaries, and ii) special triple point (in 2D) or triple line (in 3D) elements to prevent artificial dilation at these locations in the microstructure with iii) a physically-based crystal plasticity constitutive model for time-dependent inelastic deformation of the individual grains. Experimental data at various scales is used to calibrate the framework and compare with model predictions. We pay particular consideration to effects of grain boundary sliding during creep of Type 316 stainless steel, which is used extensively in structural components of the UK fleet of Advanced Gas Cooled Nuclear Reactors (AGRs). It is found that the anisotropic deformation of the grains and the mismatch in crystallogr